In order to realize the resource disposal of surplus sludge from sewage treatment plant, ordinary silicate cement was used to solidify it as a building material. The surplus sludge and cement were mixed evenly according to a certain ratio and placed in a standard curing box for 3~28 days. The unconfined compression strength (R_C) and total organic carbon (TOC) content of the sludge?cement consolidated body were used as evaluation indicators. It was found that the R_C of 28 days for surplus sludge?cement solidified block could reach about 6.9 MPa when mass ratio (R_m) of surplus sludge to ordinary silicate cement and mass ratio (R_l/s) of liquid to solid are 0.63 and 0.31. The R_C can't meet the minimum strength requirement of non?sintered brick, but meets the strength requirement for surplus sludge landfill. The total organic carbon value in leached solution (TOC_l) of surplus sludge?cement solidified block decreased by about 86% compared with the initial value (TOC₀) in consolidated block. It indicates ordinary silicate cement solidified surplus sludge can effectively solidify organics from surplus sludge in the solidified body, which can effectively inhibit the secondary pollution of surplus sludge for land in the landfill treatment process.